- 1. The inadepuats braking conditions are the main cause to produce heat-effected metal layer and fatigue crackings.
- 制动工况不当是产生热影响层和疲劳裂纹的主要原因。
youdao
- 2. Crackings occurred three times in elbow bend since one domestic long distance gas transportation pipeline came to used in 1993.
- 国内某长距离煤气输送管道于1993年投入运行以来，先后三次在管道弯头部位出现裂纹，导致煤气泄漏。
youdao
- 3. Based on the cracking mechanism and FEM, the crackings on the grade crushed stone pavement and the semirigid base asphalt pavement are compared and analyzed.
- 基于断裂力学，采用有限元程序，对两种级配碎石夹层沥青路面结构和常规半刚性基层沥青路面结构的断裂进行了对比分析。
youdao
- 4. During the formation of the South China continent, the main tectonic events had two collisions and three crackings which formed the main body of structural framework.
- 在华南大陆形成过程中，主要构造事件为两次碰撞、三次裂解的主体构造格局。
youdao
- 5. It is concluded from the analysis that the culprit of cracking is the mal-fluidization of stripping steam as all the crackings of stripping section have devel - oped near the steam.
- 认为沉降器汽提段穿孔部位均发生在汽提蒸汽附近，汽提蒸汽流化异常状态是造成穿孔的根本原因。
youdao
- 6. Two kinds of crackings show that the tensile stress induced for asymmetric temperature distribution during laser rapid forming processing is the external reason which results in cracks.
- 两种开裂都说明激光快速成形过程受热不均匀所引起的拉伸应力是产生熔覆裂纹的外在原因。
youdao